201 Stainless Steel Sheet

201 STAINLESS STEEL SHEETS The plate width: 1000 mm, 1220 mm, 1250 mm, 1500 mm and 1800 mm and 2000 mm; Thickness: cold plunge into 2 b (0.1 6.0 mm); Smooth in surface: 2 b, BA;8 k mirror;Drawing, grinding;Snowflake sand;Stainless steel without fingerprints; Decorative panel: color plate, titanium plate plating, etching plate, oil thrown hairline plate (HL, NO. 4), 3 d board, sandblasting board, embossing plate ReGaBu: stainless steel plate hot rolling NO. 1 (rolled plate, plate); Thickness: industrial No. 1 (3-159 - mm) on the surface, 8 k mirror;Drawing, titanium plating, grinding;Snowflake sand;Stainless steel without fingerprints; Corrosion resistance The general level of corrosion resistance of Type 201 is similar to Type 301. Type 201 should perform adequately as a replacement for Type 301, in most mild environments. The scaling resistance of Type 201 is less than that of Type 301. Type 201 resists destructive scaling up to about 1500 °F (816 °C), about 50 °F (28 °C) less than Type 301. Fabrication Type 201 Stainless Steel can be fabricated by bench forming, roll forming and brake bending in much the same manner as Type 301. However, because of its higher strength, it may exhibit greater springback. This material can be drawn similarly to Type 301 in most drawing operations if more power is used and the hold-down pressure is increased. Weldability The austenitic class of stainless steels is generally considered to be weldable by the common fusion and resistance techniques. Special consideration is required to avoid weld “hot cracking” by assuring formation of ferrite in the weld deposit. As with other chrome-nickel austenitic stainless steel grades where carbon is not restricted to 0.03% or below, the weld heat affected zone may be sensitized and subject to intergranular corrosion in some environments. This particular alloy is generally considered to have poorer weldability to the most common alloy of this stainless class, Type 304L Stainless Steel. When a weld filler is needed, AWS E/ER 308 is most often specified. Type 201 Stainless Steel is well known in reference literature and more information can be obtained in this way. Heat treatment Type 201 is not hardenable by heat treatment. Annealing: Anneal at 1850 – 1950 °F (1010 – 1066 °C), then water quench or rapidly air cool. The annealing temperature should be kept as low as possible, consistent with the desired properties, because Type 201 tends to scale more than Type 301

Stainless Steel grade
Grade	Chemical composition
Grade	C≤	Si≤	Mn≤	P≤	S≤	Ni	Cr
201	0.15	1.00	5.5-7.5	0.5	0.03	3.50-5.50	16.00-18.00
202	0.15	1.00	7.5-10.0	0.5	0.03	4.00-6.00	17.00-19.00
304	0.08	1.00	2.00	0.045	0.03	8.00-11.00	18.00-20.00
304L	0.03	1.00	2.00	0.045	0.03	8.00-12.00	18.00-20.00
309	0.2	1.00	2.00	0.04	0.03	12.00-15.00	22.00-24.00
309S	0.08	1.00	2.00	0.045	0.03	12.00-15.00	22.00-24.00
310	0.25	1.50	2.00	0.04	0.03	19.00-22.00	24.00-26.00
310S	0.08	1.00	2.00	0.045	0.03	19.00-22.00	24.00-26.00
316	0.08	1.00	2.00	0.045	0.03	10.00-14.00	16.00-18.00
316L	0.03	1.00	2.00	0.045	0.03	10.00-14.00	16.00-18.00
316Ti	0.08	1.00	2.00	0.045	0.03	10.00-14.00	16.00-18.00
2205	0.03	1.00	2.00	0.03	0.02	4.50-6.50	22.00-23.00
410	0.15	1.00	1.00	0.04	0.03	0.6	11.50-13.50
430	0.12	0.12	1.00	0.04	0.03	0.6	16.00-18.00

PRODUCTS DETAILS

Hot Products

321 Stainless Steel Tube Pipe

904L Stainless Steel Plate

410S Stainless Steel Coil

No.4 Stainless Steel Coil

Hot Rolled Stainless Steel Sheet Plate

310S/309S Stainless Steel Coil

Stainless Steel Reducer

410S Stainless Steel Coil

201 Stainless Steel Bar

Hot Rolled Stainless Steel Sheet Plate

Contact us